Thommy, L., Benamira, M., Jardiel, T., Gunes, V., Joubert, O. & Caldes, M. T. (2021) Ru exsolution in substituted La0.75Sr0.25Cr0.5Mn0.5O3-delta compound as anode material for an IT-SOFCs. Mater. Chem. Phys. 268 124724. 
Added by: Richard Baschera (2021-06-25 08:22:46)   Last edited by: Richard Baschera (2021-06-25 08:24:28)
Type de référence: Article
DOI: 10.1016/j.matchemphys.2021.124724
Numéro d'identification (ISBN etc.): 0254-0584
Clé BibTeX: Thommy2021
Voir tous les détails bibliographiques
Mots-clés: catalyst, Conductivity, Exsolution, lscm, methane, miec, nanoparticles, ni, oxide fuel-cell, Perovskite, SOFC anode, stable efficient anode, Surface, Symmetrical cells
Créateurs: Benamira, Caldes, Gunes, Jardiel, Joubert, Thommy
Collection: Mater. Chem. Phys.
Consultations : 1/360
Indice de consultation : 7%
Indice de popularité : 1.75%
In this study, the synthesis of La0.75Sr0.25Cr0.4Mn0.5Ru0.1O3-delta a (LSC0.4MRu0.1) compound is presented and its total conductivity is measured and compared with that of La0.75Sr0.25Cr0.5Mn0.5O3-delta (LSCM) and the Ni-substituted compound La0.75Sr0.25Cr0.5Mn0.3Ni0.2O3-delta (LSCM0.3Ni0.2). While the substitution of Ni decreased LSCM conductivity under a reducing atmosphere, an increase of the total conductivity of Ru substituted phase is evidenced. The reduction of Ni and Ru-substituted LSCM under Ar/H-2 5% up to 800 degrees C or 1000 degrees C respectively leads to the exsolution of nanoparticles, but also to a slight decomposition for the Ru-substituted compound. However, the use of these reduced materials as anode for solid oxide fuel cell (SOFC) in symmetrical cells based on Ce0.9Gd0.1O1.95 (CGO) electrolyte implies not reducing the total system at a temperature higher than 600 degrees C to avoid ceria reduction. The solution consists of pre-reducing the electrode materials at their exsolution temperature before casting them on CGO thin disk. Under reductive atmospheres, Electrochemical impedance spectroscopy study of symmetrical cells suggests that the exsolution approach improves the adsorption of gaseous species compared to LSCM. LSC0.4MRu0.1 symmetrical cell exhibits the lowest polarization resistance, 0.087 Omega cm(2) under Ar/H-2 (5%) and 0.044 Omega cm(2) under methane at 600 degrees C.