Dowuona, A. N. N., Yaya, A., Nyankson, E., Efavi, J. K., Damoah, L. N. W., Dodoo-Arhin, D., Apalangya, V., Annan, E., Tiburu, E. K., Onwona-Agyeman, B. & Tomiczek, B. (2018) Investigating triaxial electrical properties of ceramic composites for electroporcelain insulators. Journal of Ceramic Processing Research, 19 95–100. 
Added by: Richard Baschera (2018-07-24 14:20:58)   Last edited by: Richard Baschera (2018-07-24 14:36:34)
Type de référence: Article
Clé BibTeX: Dowuona2018
Voir tous les détails bibliographiques
Catégories: HORSIMN, INTERNATIONAL
Créateurs: Annan, Apalangya, Damoah, Dodoo-Arhin, Dowuona, Efavi, Nyankson, Onwona-Agyeman, Tiburu, Tomiczek, Yaya
Collection: Journal of Ceramic Processing Research
Consultations : 6/631
Indice de consultation : 5%
Indice de popularité : 1.25%
Résumé     
Four porcelain composites comprising kaolin (27-37%), beach sand (20-24%), ball clay (13-18%) and feldspar (25-40%), were formulated and characterized using powder XRD, SEM and particle size distribution analysis in order to determine their potential for use as electroporcelain insulators. Chemical, mechanical and electrical properties were also evaluated. Each of the formed samples were compressed at 200 MPa and sintered at 1250 degrees C for 1 hour. Bending strength results of the porcelain bodies showed increase in bending strength with reduction in particle sizes. An increase in dielectric strength was found for samples with a higher felspar content. The XRD pattern for all the sintered samples showed the presence of quartz and mullite phases in the body at different intensities. Samples with lower particle sizes showed similar electrical and mechanical properties to commercially available electroporcelains albeit at a cheaper cost of production.
  